HKZ300
High Pressure High Temperature Optical Floating Zone Furnace
- advanced vertical 2-mirror setup with XBO lamps (3 kW, 5 kW, 6,5 kW or 8 kW)
- 0-100 % full irradiation control with advanced power shutter
- atmosphere: Argon and oxygen (in any mixture ratio or pure), pressure up to 300 bar
- alternatively: vacuum 10-3 mbar
- samples rods up to 10 mm diameter and 120 mm length
- temperature: up to 3000 °C
- pulling rate: 0.1 mm/h to 150 mm/h
- rotation rate: 0 to 50 rpm
- afterheater available: total pressure up to 10 bar, temperature of the afterheating zone up to 1100 °C, oxygen content up to 20 %
LKZ10
High Pressure High Temperature Laser Floating Zone Furnace
- 5x 300 W diode lasers, wavelength 980 nm
- laser beam geometry: rectangular profile with 4 x 8 mm²
- atmosphere: Argon and oxygen (in any mixture ratio or pure), pressure up to 10 bar
- samples rods up to 10 mm diameter and 170 mm length
- temperature: up to 3000 °C
- pulling rate: 0.1 mm/h to 50 mm/h
- rotation rate: 0 to 50 rpm
AHSO
Advanced High Pressure Oxygen Furnace
- Annealing oxide rods at temperatures up to 1100 °C and pressure up to 200 bar
- super-fast quenching of metastable phases at high pressures
- atmosphere: Argon and oxygen (in any mixture ratio or pure)
- samples rods up to 10 mm diameter and 100 mm length
Your Workflow with Dresden Materials
Pre- and Post-processing of your sample rods in the AHSO
(use as stand-alone system also possible)
Crystal Growth in the HKZ300 or LKZ10
Reserve time slots and conduct your experiment with our technical support
Make use of the "remote experiment" option to save travel time and costs
Test new parameters on your samples and processes